Brand Name : Deze
Model Number : 410
Certification : SGS , BV
Place of Origin : China
MOQ : 2 tons
Price : Negotiated
Payment Terms : L/C, T/T, Western Union
Supply Ability : 1000 tons per month
Delivery Time : 10-15 days
Packaging Details : Plastic film+waterproof paper+pallet
Name : 410 Stainless Steel Pipe
Grade : 410
Type : Pipe
Technique : Welded
Standard : AISI
Diameter : 6mm - 630mm
Thickness : 0.5mm - 100mm
Length : 1000mm - 6000mm
AISI ASTM JIS SUS 410 410S Stainless Steel Welded Round Pipe Tubes
410 Stainless Steel Welded Pipe Overview:
410 stainless steel pipe is made up of martensitic steel. Martensitic steels are used when the strength and toughness are needed along with high wear and tear resistance. Their corrosion resistance is lower than the austenitic stainless steels in general. The 410 stainless steel pipe material has carbon, manganese, silicon, phosphorus, sulfur, chromium and nickel in its material composition. This specific composition provides it with the high wear and tear resistance. Any 410 grade pipe can be manufactured through cold drawing as 410 seamless pipe or through electric resistance weld or through electric fusion weld. The 410 stainless steel pipe dimensions vary according to the manufacturing methods as well.
410 Stainless Steel Welded Pipe Physical Properties:
Magnetic Permeability | 0.28 lb/in3 7.73 g/cm3 |
Specific Heat | 0.11 BTU/lb-°F (32 – 212°F) 0.46 J/kg-°K (0 – 100°C) |
Modulus of Elasticity | 29 x 106 psi 200 GPa |
Thermal Conductivity 212°F (100°C) | 187 BTU/hr/ft2/ft/°F 26.9 W/m-°K |
Melting Range | 2700 – 2790°F 1480 – 1530°C |
Electrical Resistivity | 23.7 Microhm-in at 68°C 60 Microhm-cm at 20°C |
410 Stainless Steel Welded Pipe Mechanical Properties:
Material Grade | Material Number | Tensile Strength | Yield Strength Ksi (MPa) | Elongation | Brinell Hardness | Rockwell Hardness |
TP410 | S41000 | 60 (415) | 30 (205) | 20 | 207 | 95 |
410 Stainless Steel Welded Pipe Corrosion Resistance:
410 stainless steel resists dry atmosphere, fresh water, mild alkalies and acids, food, steam and hot gases. Must be hardened for maximum heat and corrosion resistance. Performance is best with a smooth surface finish. Less corrosion resistant than the austenitic grades and also less than 17% chromium ferritic alloys such as Grade 430.
410 Stainless Steel Welded Pipe Heat Treatment:
1. 410 Stainless Steel Annealing
Full anneal – 815-900°C, slow furnace cool to 600°C and then air cool.
Process Anneal – 650-760°C and air cool.
2. 410 Stainless Steel Hardening
Heat to 925-1010°C, followed by quenching in oil or air. Oil quenching is necessary for heavy sections. Temper, generally within the range 200-400°C, to obtain a wide variety of hardness values and mechanical properties as indicated in the accompanying table.
The tempering range 400-580°C should generally be avoided.
![]() |