2B Finish Cold Rolled Slit ASTM 410S Stainless Steel Sheet Coil
410S Stainless Steel Coil Characteristics:
Stainless steel 410S is produced in accordance with the American ASTM standard of stainless steel, equivalent to China's 1Cr13 stainless steel, S41000 (AISI, ASTM).
0.15% carbon, 13% chromium,410S stainless steel: good corrosion resistance, machinability, general purpose blade, valve type.
Heat treatment of stainless steel: solution treatment (℃) 800-900 slow cooling or 750 fast cooling
410S Stainless Steel Coil Chemical Analysis Weight % (all values are maximum unless a range is otherwise indicated)
| Nickel | 0.6 | Silicon | 1.0 |
| Chromium | 11.5 min.- 13.5 max. | Phosphorus | 0.04 |
| Molybdenum | - | Sulfur | 0.03 |
| Nitrogen | - | Carbon | 0.08 |
| Manganese | 1 | Iron | Balance |
410S Stainless Steel Coil Features:
1) High strength
2) Excellent machinability
3) Hardened after heat treatment
4) Magnetic
5) not suitable for harsh corrosive environment
Scope of application
General blade, mechanical parts, class 1 tableware (spoon, fork, knife, etc.).
410S Stainless Steel Coil Corrosion Resistance:
The corrosion resistance of 410S stainless steel is similar to type 410. It resists corrosion in atmospheric conditions, fresh water, mild organic and mineral acids, alkalis and some chemicals. It’s exposure to chlorides in everyday activities (e.g., food preparation, sports activities, etc.) is generally satisfactory when proper cleaning is performed after exposure to use.
General Corrosion Behavior Compared With Other Non-austenitic Stainless Steels*
5% Test
Solution at 120°F
(49°C) | Corrosion Rate in Mils per Year and Millimeters per Year (mm/a) |
| Alloy 409 | Alloy 410S | Alloy 420 | Alloy 425 Mod | Alloy 440A | Alloy 430 |
| Acetic Acid | 0.88
(0.022) | 0.079
(0.002) | 1.11
(0.028) | 4.79
(0.122) | 2.31
(0.0586) | 0.025
(0.0006) |
| Phosphoric Acid | 0.59
(0.002) | 0.062
(0.002) | 0.068
(0.002) | 0.593
(0.015) | 0.350
(0.009) | 0.029
(0.001) |
*Hardened martensitic grades were tested after tempering at 400°F (204°C)
As shown in the above table, 410S has good corrosion resistance to low concentratiions of mild organic and mineral acids.
Oxidation Resistance
The oxidation resistance of 410S stainless steel is good. It can be used in continuous service up to 1300°F (705°C). Scaling becomes excessive above 1500°F (811°C) in intermittent service.
Formability
410S stainless steel can be easily formed by spinning, bending and roll forming.
410S Stainless Steel Coil Applications:
1. Petroleum Refining and Petrochemical Processing
2. Columns
3. Distillation trays
4. Heat exchangers
5. Towers
6. Ore Processing
7. Mining machinery
8. Thermal Processing
9. Annealing boxes
10. Partitions
11. Quenching racks
12. Gate valves
13. Press plates